Model NO.: various Morphology: Water Emulsion Material: Polysulfide Main Agent Composition: Thixotropic Polysulphide Promoter Composition: Curing Agent Color: Black Sealant Color: According to Your Requirements Shelf Life: 12 Monthes Specification: ISO9001/TS16949 HS Code: 522338 Bonding Function: Underwater Adhesive Application: Construction, Insulating Glass Classification: Room Curing Characteristic: Waterproof Composition: Organic Material Export Markets: Global OEM & ODM Service: Yes Trademark: jianfeng Origin: Hebei, China Contact information
Sales Manager: kent
Mobile Phone: +86-15233296877
Tel: 86-318-5106277
Fax: 86-0318-5106277
Website: www.prolianz.com
Company: Hengshui Jianfeng Engineering Rubber co., LTD.
Product Use:
1: Glue-coating before glue coping withered material surface cleaning, clean before coating. Otherwise, it will affect the adhesive seal.
2: Takes out A and B two components according to 10: 1 proportion to carry on the mix agitation to be even, achieves the achromatism.
3: Manual or mechanical operation must arrange a direction coating and put some pressure, prevent the air wrapped into.
4: Construction of the ambient temperature maintained at above 5 ° C
Packaging into large, medium and small 1, large package: Group A[300KG] Group B [33.3KG] 2, medium package: Group A[30KG] Group B[3.35KG] 3, small package: Group A[4.5KG × 5 barrels of group B were] Group B[0.5KG × 5] |
Product features
1, Has a good weather ability, durability, use a long time no cracks;
2,To the sealed components it has fully stable adhesion and durable adhesion, coagulation in water soil have long-term adhesion;
3,Water vapor transmittance is extremely low, the two-component
Polysulfide Sealant has very good waterproof function;
4,Against fungi, best bacteria resistance;
5,Good construction work, the two-component polysulfide sealant can be fill into the joint very good.
6. no produce pollution for the sealing structure, no corrosion, and the two-component polysulfide sealant has no harm to human body.
Under the conditions of the 23±2 °C and the R.H. 50±5% |
Item | Component A | Component B |
Viscosity(Pa's) | 4000 | 800 |
Appearance | Fine, smooth and homogeneous | fine, smooth and grease-like |
Color | White | Black |
Density(g/em 3 ) | 1.75±0.1 | 1.52±0.1 |
Mixed Component A and Component B at 10:1 by weight, under the conditions of 23±2 °C and the R.H. of 50±5% |
Item | Standard | Result | Test method |
Resistance to flow, mm | Vertical | ≤3 | 0.8 | GB/T 1 13477 |
Level | No distortion | No distortion |
Application Time, 30min ,S | ≤10 | 4.8 | |
A:B=10:1, Under the conditions of the 23±2 °C and the R.H. of 50±5%, after 7days of curing: |
Item | Standard | Result | Test method |
Durometer hardness (Shore A) | | 45 | GB/T 1 531 |
Tensile strength , MPa | MPa | 0.8 | GB/T 1 13477 |
Permeation rate of evaporation (g/m 2 .d) | ≤15 | 8 | GB/T 1 1037 |
GB/T 1 13477 | | 25HM | JC/T 1 486 |
Contact us if you need more details on Polysulfide Sealant. We are ready to answer your questions on packaging, logistics, certification or any other aspects about
Two Component Polysulfide Sealant、
Two Component Thiokol Sealant. If these products fail to match your need, please contact us and we would like to provide relevant information.
Product Categories : Waterproof Sealant Series > Polusulfide Sealant