New Products
Find Polysulfide Sealant, Two Component Polysulfide Sealant, Two Component Thiokol Sealant on Industry Directory, Reliable Manufacturer/Supplier/Factory from China.
Payment Type: | L/C, T/T, Western Union, Paypal |
---|---|
Min. Order: | 10 |
Model No.: various
Product Use: 1: Glue-coating before glue coping withered material surface cleaning, clean before coating. Otherwise, it will affect the adhesive seal. 2: Takes out A and B two components according to 10: 1 proportion to carry on the mix agitation to be even, achieves the achromatism. 3: Manual or mechanical operation must arrange a direction coating and put some pressure, prevent the air wrapped into. 4: Construction of the ambient temperature maintained at above 5 ° C |
Packaging into large, medium and small 1, large package: Group A[300KG] Group B [33.3KG] 2, medium package: Group A[30KG] Group B[3.35KG] 3, small package: Group A[4.5KG × 5 barrels of group B were] Group B[0.5KG × 5] |
Product Characteristics Solvent free: Don't produce any volatile compound. Outstanding thixotropism, suitable for all-wave construction. Low tack: Construction craftwork is simple and improve efficiency, cost reduction. After solidification, it form elastomer, which has excellent cohesion to glass and aluminum alloy etc metal. Suitable for all kinds of climate: It could keep its characteristics from -50 ° Cto 100° C and could construct from -5° C to 45° C. It has compatibility with all kinds of hot melt butyl, suitable for the manufacture of double times sealing of insulating glass. |
Storage Life Please keep in cool and dry place below 27° C to extend the validity of product, the validity period is 12 months. Mode of Transportation This product is nonflammable, nonexplosive, non-toxicity, it could transport by train, vehicle, ship, airplane etc. Serious Statement: This product cannot be used as structural cohesiveness of curtain wall, sunroof, sun room, frosted glass. |
Under the conditions of the 23±2 °C and the R.H. 50±5% | ||||||
Item | Component A | Component B | ||||
Viscosity(Pa's) | 4000 | 800 | ||||
Appearance | Fine, smooth and homogeneous | fine, smooth and grease-like | ||||
Color | White | Black | ||||
Density(g/em 3 ) | 1.75±0.1 | 1.52±0.1 | ||||
Mixed Component A and Component B at 10:1 by weight, under the conditions of 23±2 °C and the R.H. of 50±5% | ||||||
Item | Standard | Result | Test method | |||
Resistance to flow, mm | Vertical | ≤3 | 0.8 | GB/T 1 13477 | ||
Level | No distortion | No distortion | ||||
Application Time, 30min ,S | ≤10 | 4.8 | ||||
A:B=10:1, Under the conditions of the 23±2 °C and the R.H. of 50±5%, after 7days of curing: | ||||||
Item | Standard | Result | Test method | |||
Durometer hardness (Shore A) | 45 | GB/T 1 531 | ||||
Tensile strength , MPa | MPa | 0.8 | GB/T 1 13477 | |||
Permeation rate of evaporation (g/m 2 .d) | ≤15 | 8 | GB/T 1 1037 | |||
GB/T 1 13477 | 25HM | JC/T 1 486 |
Product Categories : Waterproof Sealant Series > Polusulfide Sealant